Selective etching of aluminum

ABSTRACT

A process for selectively etching an aluminum-containing coating in preference to a masking material on a surface of the aluminum-containing coating by positioning a patterned masking material on the aluminum-containing coating in a radio frequency plasma etching chamber and introducing an etchant gas and a source of oxygen and silicon to the interior of the chamber under conditions where silicon dioxide is deposited selectively on masking material layer while the unmasked aluminum-containing coating is etched.

TECHNICAL FIELD

This invention relates to integrated circuit fabrication and, in particular, to aluminum and aluminum alloy etching.

BACKGROUND OF THE INVENTION

Attention is directed to my co-pending patent application entitled "Process for Selectively Etching Silicon" filed May 25, 1982, herein incorporated by reference.

Aluminum and alloys of aluminum with silicon and/or copper are widely used in integrated circuit metallization, and consequently a great deal of effort has been expended on dry etch processes which will enable fine Al patterns to be formed. The general approach which has been adopted is reactive sputter etching using an etch gas that reacts with Al to form a volatile reaction product when it is excited by an rf discharge.

For an example of the reactive sputter etching technique, see U.S. Pat. No. 3,994,793 issued to Harvilchuck on Nov. 30, 1976. Unfortunately, the only easily volatile Al compound is AlCl₃, and the requisite Cl in the discharge is exceptionally reactive with bare (unoxidized) Al. This reactivity results in loading effects and in lateral etching under the mask. In addition, the AlCl₃ residues are hygroscopic and form HCl upon air exposure which further attacks the metal. In contrast the native Al₂ O₃ oxide layer is typically etched very slowly in Cl discharges, leading to long etch "initiation" times and to grain boundary images which propagate into the substrate.

Reactive sputter etching of Al thus has problems which are mainly related to the high reactivity of Cl₂ with Al. One remedy which has been proposed is to etch the Al patterns using nonreactive sputter etching or ion milling. However, these processes redeposit the etched metal on mask sidewalls, and have poor etch rate selectivity between materials. In addition, mask profiles are altered by "faceting", and substrates are anomalously etched near metal lines ("trenching").

It should be noted that a variety of ionic species have been used in reactive sputter etching of semiconductor materials (as opposed to aluminum or aluminum alloys). Considerable efforts have been made to develop selective etching techniques for semiconductors that can, for example, etch silicon dioxide more rapidly than silicon or, conversely, remove silicon from a surface faster than SiO₂. See, for example, U.S. Pat. No. 4,213,813 issued to Lemons on July 22, 1980, wherein additives such as O₂ are proposed to achieve selective etching. I am not aware of any prior teachings of the use of such additives in connection with aluminum etching.

There exists a need for selective etching techniques for aluminum that would permit the formation of fine Al patterns. Additionally there exists a need for new etchants that are more controllable and less corrosive than chlorine-based aluminum etches.

SUMMARY OF THE INVENTION

A new technique for sputter etching of Al is described which can pattern fine lines in Al or in Al-Cu-Si alloy but does not have many of the problems associated with presently available reactive sputter etching methods. The technique combines deposition and etching in the one process; Al₂ O₃, Al, and Al-Cu-Si alloy are etched, while all other materials are coated with a layer of SiO_(x). This results in essentially infinite (Al/mask) and (Al/substrate) etch rate ratios. In addition, the etch gas contains no Cl, which is a common cause of corrosion and undercut.

The gas described here is a SiF₄ /O₂ mixture, and it is shown that additions of most impurity gases have very little effect on the etch. Water or H₂ addition is, however, beneficial and typical profiles are shown for a SiF₄ /O₂ /H₂ mixture with Cr and photoresist masking layers. This etch "squares off" photoresist profiles, resulting in linewidth shrinkage by an amount dependent on the initial photoresist edge slope. The SiO_(x) coating forms peaked structures on the masking layer and can be stripped after the sputtering process with selective wet etchants to expose the photoresist and the underlying Al pattern.

BRIEF DESCRIPTION OF THE FIGURES

FIG. 1 is a schematic diagram of the steps in my aluminum etching method.

FIG. 2 is a graph of etching and coating rates versus partial pressure of O₂ in a high pressure SiF₄ discharge according to my invention.

FIG. 3 is a graph of etching and coating rates versus partial pressure of O₂ in a low pressure SiF₄ discharge according to my invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

In FIG. 1 the process of my invention is shown schematically. In the first step a resist is deposited on an aluminum-coated substrate wherein an aluminum strip is ultimately desired. In the second step etching begins and proceeds until all the aluminum not covered by resist is removed. At the same time an SiO_(x) coating is built-up on top of the resist-covered structures. After the uncovered Al is etched to completion, continuation coats the entire surface with SiO_(x). The coating forms less easily adjacent to etched structures probably because of shadowing and "trenching" or "dovetailing" processes, which are caused by reflection of sputtering particles from a sloping sidewall to the surface below, resulting in an enhanced etch rate near the sidewall. Removal of the SiO_(x) coating from the Al sidewall and from the substrate results in some attack of the substrate, and this attack will be most pronounced where the SiO_(x) coating was thinnest. Hence, in cases where this attack is undesirable, the sputtering over-etch time should be limited. The SiO_(x) coating is then removed by wet etching and after SiO_(x) removal the photoresist is removed in a hot resist stripping solution.

A standard sputtering system was used in my experiments modified to accept a 10 cm-dia. Si target. In this configuration the dc bias voltage was 1/2 of the rf peak-to-peak voltage. Etch rates were measured from stylus traces over regions masked by small Si chips or by thin layers of the material to be measured. The etch rate of a patterned material was sometimes affected by the choice of substrate so, for consistency in FIGS. 2 and 3, results for Si substrates are given. All samples were contacted to the target using diffusion pump oil since substrate temperature affects both the etch and SiO_(x) coating rates.

FIG. 2 shows the dependence of etch and coating rates on O₂ partial pressure in a 4 Pa SiF₄ discharge. O₂ combines with Si from the discharge to form SiO_(x), and three factors determine whether a surface will be coated: (a) the available SiO_(x) generation rate in the discharge: (b) the probability of SiO_(x) formation on the surface: and (c) the probability of the deposited SiO_(x) being resputtered. The first factor is controlled partly by the O₂ partial pressure, since progressively more materials become coated as the O₂ partial pressure rises. Of course, all coated surfaces are alike and have the same coating rate: this rate appears to be controlled by factors (b) and (c). (The variability of this coating rate will be discussed later).

Further studies were made at a lower SiF₄ gas flow rate (of 0.01 Pa m³ s⁻¹) and 0.5 Pa SiF₄ pressure. FIG. 3 shows the variation of etching characteristics with O₂ partial pressure; these results are similar to those obtained at 4 Pa SiF₄ pressure. The effects of gas additions are shown in Table 1.

                  TABLE 1                                                          ______________________________________                                         Al etch and SiO.sub.x coating rates with various                               gases added to a 0.5 Pa SiF.sub.4 discharge with                               Si target held at 2.6 kV.sub.p-p.                                                              SiO.sub.x Coating                                                                          Al etch                                            Conditions      Rate (nm s.sup.-1)                                                                         Rate (nm s.sup.-1)                                 ______________________________________                                         No additions    (Si was etched)                                                                            0.4                                                0.25 Pa O.sub.2, long pumpout                                                                  0.012       0.37-0.44                                          0.25 Pa O.sub.2, standard                                                                      0.08-0.17   0.33-0.42                                          0.25 Pa O.sub.2, 4° C. target                                                           0.02-0.22    0.4-0.48                                          0.15 Pa H.sub.2 O                                                                              0.65-0.7    0.29                                               0.25 Pa O.sub.2, 0.25 Pa H.sub.2                                                               0.52-0.6     0.3-0.33                                          0.25 Pa O.sub.2, 0.22 Pa CHF.sub.3                                                             (Se was etched)                                                                            0.38-0.48                                          0.25 Pa O.sub.2, 0.08 Pa N.sub.2                                                               0.12        0.36                                               0.5  Pa CO      (slight coating)                                                                           0.19                                               0.25 Pa O.sub.2, 0.035 Pa He                                                                   0.26-0.3    0.44                                               ______________________________________                                    

Note that with all gases but CO, the Al etch rate is roughly constant. However, the SiO_(x) coating rate is strongly affected by H₂ and H₂ O additions. Variations in chamber pump-out time result in variations in the residual H₂ O level, and this is the probable cause of the observed coating rate variability. The mechanism of this H₂ --SiO_(x) interaction is not clear; HF may be formed thus liberating more free Si, or H may catalyse reactions in the discharge or on the surfaces.

The SiO_(x) coating can be removed after sputter etching with any HF-containing solution. However, since the Al etch rate must be minimized to retain good line definition, the typical etch must have a high (SiO_(x) /Al) etch rate ratio. Buffered HF has a ratio of ˜43, whereas the modified buffered HF solution available from Transene Corporation of Rowley, MA has a ratio of 500-650. The SiO_(x) layer is etched rapidly in comparison with fused quartz, indicating high porosity. 

What I claim is:
 1. The process for selectively etching an aluminum-containing coating in preference to a masking material on a surface of said aluminum-containing coating which comprises coating a substrate with an aluminum-containing material, positioning a patterned masking material on said aluminum-containing coating, positioning said substrate on a target connected to a radio frequency electrode, introducing an etchant gas composition into said chamber under conditions to convert said etchant gas composition to a plasma, providing a source of oxygen and silicon to the interior of said chamber under conditions to deposit silicon dioxide selectively on said masking material layer and to etch said aluminum-containing coating not covered by said masking layer selectively.
 2. The process of claim 1 wherein said masking material is a photoresist.
 3. The process of claim 1 wherein said etchant gas is SiF₄ as a source of silicon.
 4. The process of claim 1 wherein the process further comprises providing a source of hydrogen to interior of said chamber. 